Double Coated Copper free Mirror respects environment by avoiding copper in the manufacturing process also uses paint coating having lead content <0.5%.

 As well as being environmentally friendly compared with conventional mirrors. Grand Copper and lead free mirror gives far greater resistance to natural atmospheric corrosion which offers up to 3-5 times more protection against corrosion, chemicals moisture and abrasion than traditional mirror. it survives 120 hours in CASS test and 480 hours in 100% humidity without any deterioration The protection reduces the unsightly incidence of problems of black edges and spot faults particularly in locations such as bathrooms.

 

Features

● True image reflectance with virtually no distortion

●     High optical quality and durability

●    Environmentally friendly

●     Easy to be cut, drilled, beveled, polished without oxidation and rusting.

●     High heat resistance, which can be used in environments up to 60°C

●     High moisture resistance

●   High scratch resistance

 

Application

●  Wardrobe door

●    Bathroom mirrors

●    Display cases

●     Fitness/dance studio

●    Surface and tables

 Specification

●   Colors can be clear, bronze, grey, green, blue

●   Back paint can be grey, green, blue, white

●     Thickness can be 3-8mm

●  Size can be 50*50mm to 3660*2440mm.

Parameter	Test	Test Standard	Acceptance Criteria
Resistance to Corroision	CASS Test	ISO 9227	Edge Corrosion Number of Spots	After 120hrs <2.5mm After 120hrs 2 of diameter >0.3mm & < 3 mm 3 of diameter < 0.3 mm
Resistance to Humidity	Condensation Water Test	ISO 6270-2	Edge Corrosion Number of Spots	After 480hrs < 0.2mm After 480hrs 1 of diameter < 0.3mm

 

Characteristics	Criteria	Reference
Reflectance	Min 83%	BS EN 1036:1999
Silver Film Weight	Min 700 mg/m2	BS EN 1036:1999
Paint Coating Thickness	Min 45 Micron	BS EN 1036:1999
Paint adhesion	Min Grade 2	ISO 2409:2007 (E)